General
Customer
UsefulThis listing is for PRO-SET INF-114 Infusion Resin only. You will need to select the appropriate PRO-SET Infusion Hardener from one of the suggested hardeners listed below.
PRO-SET INF-210 Fast Infusion Hardener - Pot Life: 27 min*
PRO-SET INF-211 Medium Infusion Hardener - Pot Life: 122 min*
PRO-SET INF-212 Slow Infusion Hardener - Pot Life: 185 min*
PRO-SET INF-213 Extra-Slow Infusion Hardener - Pot Life: 262 min*
*Pot Life is calculated using 150g @ 77°F (25°C)
** If any of the above links do not take you to a product listing, it would indicate that product is not in stock.
PRO-SET Infusion Epoxies are super low viscosity systems with a range of hardeners to meet the demands of modern infusion processes.
STANDARD INFUSION SYSTEMS
PRO-SET Infusion Epoxies accommodate a vast range of process needs with a single resin and four hardeners. PRO-SET Infusion hardeners range from fast to extra slow, and may be blended to provide even greater versatility with your custom processes.
Choose resin by viscosity and hardener by speed.
Infusion Epoxies Hardeners may be blended for targeted cure time. Infusion process PRO-SET Infusion Epoxies result in lightweight, high performance composites that will withstand long term cyclic loading in the harshest environments. PRO-SET Infusion Epoxies develop excellent physical properties at room temperature and may be post-cured to further enhance performance.
Infusion Epoxies can be dyed, upon request, to provide for visual quality control. A yellow dye in the resin and a blue dye in the hardener, when properly metered and thoroughly mixed, will result in a consistent shade of green.
INF Resin Selection
| Property | Standard | Units | INF-114 Resin1 |
| Mix Ratio by Volume | R:H | 3:1 | |
| Mix Ratio by Weight | R:H | ~3.65:1 | |
| Mixed Viscosity @ 77°F (25°C) | ASTM D2196 | cP | ~245 |
| Mixed Density @ 72°F (22°C) | lb/gal (g/cc) | ~9.52 (1.14) | |
| Compression Yield | ASTM D695 | psi (MPa) | ~14,100 (97.0) |
| Tensile Strength | ASTM D638 | psi (MPa) | ~10,400 (71.7) |
| Tensile Modulus | ASTM D638 | psi (GPa) | ~4.90E+05 (3.38) |
| Tensile Elongation | ASTM D638 | % | ~4.95 |
| Flexural Strength | ASTM D790 | psi (MPa) | ~18,000 (124) |
| Flexural Modulus | ASTM D790 | psi (GPa) | ~4.63E+05 (3.19) |
| Tg Ultimate via DMA2 | ASTM E16403 | °F (°C) | >193 (85.2) |
| Tg Ultimate via DSC with INF-251-HT Hardener2 | ASTM E16403 | °F (°C) | 264 (129) |
1Average of properties for combinations with INF-210, INF-211, INF-212 and INF-213 Hardeners.
2 Additional post cure may be required; contact the Gougeon Technical Staff for details.
3 1 HZ, 3°C per minute
Typical Physical Properties Comparison Guide
Test specimens are cured at room temperature to gelation and 180°F (82°C) for eight hours, unless otherwise noted. Neat epoxy samples are used for testing. See Resin/Hardener Technical Data Sheet for exact values. Typical values, not to be construed as specifications.
PRO-SET INF-114 Epoxy with INF-210 Hardener TDS PRO-SET INF-114 Epoxy with INF-211 Hardener TDS PRO-SET INF-114 Epoxy with INF-212 Hardener TDS PRO-SET INF-114 Epoxy with INF-213 Hardener TDS PRO-SET INF-114 Epoxy with INF-251-HT Hardener TDS
Epoxy Mixing Guide