LOW TEMP CURING 2x2 Twill Carbon Fiber Fabric/Cloth 50" 3k 6oz 203gsm Single Sided PREPREG. This Fabric is Toray T300 carbon fiber. This fabric has a width of 50", tow size of 3k and is woven in a 2x2 twill weave. This is the most widely used pattern in the automotive industry. This material is woven tighter than most of our competitors' fabrics. This will help ensure a straight weave and a better looking final product.
This LOW TEMP Pre-impregnated carbon fiber reinforcement makes part production efficient and allows for more complex parts to be produced vs standard infusion or vacuum bagging techniques as the epoxy is already in the fabric. This special epoxy blend allows for low temp curing options down to 150deg F. This allows for the use of curing in a paint booth as well as using low temp materials for making tools. Higher temperatures are hard on tooling so lower temperatures are preferred if you have the time to wait. The carbon material in the prepreg is our model F-1835 6oz 3k 2x2 Twill weave that has been coated with epoxy. Prepreg is easier to use and allows you to piece sections together to create seams that look clean and professional. To use this material just cut to shape, pull off the plastic liner, place in mold, vacuum bag the material down and ramp up the heat at the desired rate below for proper amount of time and your part is done. The material has a 42% resin/fiber ratio. This material is a single sided tack material meaning that resin is on one side. Customers attempting to do roll wrapping should use a double sided prepreg. To achieve a higher quality class A finish, we have clear surfacing films that are compatible with this resin system. This will allow you to have a resin rich surface.
This product is 50" wide and sold in 5 yard, 10 yard, 25 yard & 50 yard segments. We do not sell this by the cut yard because it is stored in a freezer and must stay frozen to comply with shelf life requirements.
• Cure temperature from 150°F to 250°F
• Service temperature up to 275°F after post cure
• Low CTE and shrinkage
• Work life at 70°C: 21 days
• Storage life at 0°F: 12 months
• Very low VOC content – no added solvents during manufacture
Storage & Out Life
This material should be kept frozen at 0°F. It must be kept sealed in a polythene bag which must not be opened until fully thawed to room temperature. If the material is not fully used, then the material must be resealed in the polythene bag to prevent moisture absorption.
Cure Cycles & Performances
|Cure||Initial Min Cure||Tg|
• Curing Schedule is meant to be a guide only and is subject to local conditions.
• To avoid exotherm particular care must be taken with thick laminates.
Ramp rates must not exceed 5°F per minute during initial cure.
Ramp rates must not exceed 1°F per minute during post cure (free standing).
|Separator||Release paper and poly film|
|Shelf Life||One year at 0°F|
|21 Days at 68°F|
|Material Warp||Carbon Fiber|
|Material Weft||Carbon Fiber|
|Weave||2 x 2 Twill|
|Ends Per Inch||13|
|Pics Per Inch||13|
|Yarn Size Warp||3k|
|Yarn Size Weft||3k|
|Weight||6oz / 203gsm|
|Width||50" / 127cm|
Volatile content < 1.0%
Fiber volume fraction 50 to 60%
Voidage (autoclave cure) < 1.0%
|Tests performed on PREG301S-42%-C200T-T300-2X2T-3K-42%RW laminates|
|Mechanical Property||Test Method||Test Condition||Test Values|
|Tensile Strength||BS EN ISO 527-4:1997||@ 80°F dry||573 MPa|
|Tensile Modulus||BS EN ISO 527-4:1997||@ 80°F dry||52.7 GPa|
|Compressive Strength||BS EN ISO 14126:1999||@ 80°F dry||631 MPa|
|Flexural Strength||BS EN ISO 14125:1998||@ 80°F dry||863 MPa|
|Flexural Modulus||BS EN ISO 14125:1998||@ 80°F dry||51.7 GPa|
|Interlaminar Shear Strength||BS EN 2563:1997||@ 80°F dry||74.0 MPa|
Application: Remove material from cold storage until material is properly thawed at room temp. Keep the material wrapped to prevent moisture from condensing on the adhesive. Cut prepreg to the correct size, remove poly film from one side and apply to part or mold. Then remove the backing paper. Continue until the desired number of plies are obtained. When your lay-up is finished, you need to cure the material in a vacuum bag placed inside an oven or autoclave. Compression molding via press is also a proper way to cure this prepreg. Make sure to use appropriate release films, and bagging materials depending on type of cure or heat/pressure applied.
Health and Safety
This material contains epoxy resin which can cause allergic reactions with skin contact and must avoid repeated and prolonged skin contact.
Please refer to the product Safety Data Sheet before using this material. The following precautions must be taken when using epoxy resin prepregs:
• Overalls must be worn.
• Impervious gloves must be worn.
• Curing schedule is meant to be as a guide only and is subject to local conditions.
• To avoid exotherm, particular care must be taken with thick laminates.
• Ramp rates must not exceed 5°F/min during initial cure and 1°F/min during post cure.
Shipping: This material should be shipped expedited airmail. Due to a short shelf life at room temp we suggest shipping this material via an expedited service such as UPS Overnight, 2-day or 3-day. These are guaranteed services. If these are chosen, we will ship the materials in the beginning of the week to ensure they do not sit in the shipping company warehouse over the weekend. We can send the material with insulation and icepacks at an additional cost (add $25 per ITEM for ice packs and insulation). It is suggested that you ship with ice packs and 2-day airmail at a minimum. If you plan to use material within days of arrival or are OK with loosing days of shelf life, you can select any shipping method you would like, however if our minimum suggested shipping method is not chosen, we will not be held responsible for issues with material.
Custom Prepreg Options
We can have almost any of our fabrics pre-impregnated for you. Please email us for more details. We have systems in our PREG3xx series that can cure at various temps from 86° F to 275° F with safe service temps of over 600° F. We can do a max width of 60" and also offer toughened systems. Lead times are usually 2-3 weeks for custom prepreg. We can do single side or double sided prepreg, vary the resin % in the cloth and vary the tack level of the material. Options are endless.