Carbon Fiber Fabric Plain Weave HIGH MODULUS 6k 50"/127cm 5.9oz/200gsm

Model:
F-4966-50
Unit of Measure:
Linear Yard
Shipping:
Ships to USA Only
$110.40

This fabric is made from HIGH MODULUS Toray M46JB Yarn and has a width of 50", tow size of 6k and is woven in a plain weave. The 6k High Modulus Carbon Yarn is a more finer looking yarn than a normal 6k Carbon yarn. The results of this is the fabric has an appearance of a 3k product. It has a very unique visual appearance with a thickness of only .009". This fabric is great for structural buildup and will yield a much stiffer product than a standard modulus 200 gsm fabric.

How we sell

This roll is 50" (127cm) wide and the fabric is sold by the linear yard. The unit price displayed is for 1 linear yard, all volume discounts will be automatically applied when selecting larger quantities of fabric when added to your shopping cart, as indicated in the table above with quantity discount ranges for units purchased.

Please purchase the number of linear yards that you require. When purchasing multiple yards of the same fabric you will receive one continuous length of that material. We carefully take that material and roll it onto a cardboard core and wrap over with clear plastic or Kraft paper, making sure to keep the fabric in its first quality condition. We pride ourselves as having one of the best material handing crews possible. We have most of our material available for purchase in sample swatch books per fabric category. Samples of our fabrics can be purchased by Clicking this Link.

Product Specs  
Unit of Measure Linear Yard
Material Warp Carbon Fiber
Material Weft Carbon Fiber
Weave Plain Weave
Ends Per Inch 11.4
Pics Per Inch 11.4
Yarn Size Warp 6k
Yarn Size Weft 6k
Tow Size 6k
Weight 5.9oz/200gsm
Thickness .009"/.23mm
Width 50"/127cm
Resin Consumption @ 45% Resin to Fabric by Weight 4.8opsy/162gsm
The resin consumption provided is for the approximate amount of resin by weight, contained in the final part after processing by vacuum infusion. This does not account for the resin used in the flow lines and consumables such as flow media or breather cloth. Wet-layup by hand will also have a higher resin consumption in the final part and is dependent upon users techniques. Vacuum bagging a wet layup will improve the resin content. Too much resin will cause a weaker part, NOT stronger. Average rule of thumb is around 45% (+/- a couple percent). To calculate actual resin % in your part a burn test is used. For example you have a part weighing 100 grams, you would burn off the resin which would leave the fiber behind. You should have 55 grams of fiber left when your process is working correctly. Due to the variables in processing it is hard to give an accurate amount of resin needed to purchase for making your part. However you will have waste no matter what method is used. A suggested ratio is about 1-1.5lbs of resin per lb of fabric purchased.

 