Carbon Fiber Fabric 2x2 Twill PREPREG Double Sided 6k 50"/127cm 11oz/372gsm

Minimum Purchase:
5 units
Unit of Measure:
Linear Yard
Ships to USA Only

Out of stock

Quantity Buy 10 - 24 Buy 25 - 49 Buy 50 or above
Per Linear Yard $ 69.88 $ 66.97 $ 65.51
Bulk Pricing
Per Linear Yard
Buy 10 - 24
Buy 25 - 49
Buy 50 or above
$ 69.88
$ 66.97
$ 65.51

2x2 Twill Carbon Fiber Fabric/Cloth 50" 6k 11oz. This fabric has a width of 50", tow size of 6k and is woven in a 2x2 twill weave. This is the most widely used pattern in the automotive industry. This material is woven tighter than most of our competitors' fabrics. This will help ensure a straight weave and a better looking final product.

This material is a high grade PAN fiber, which means you are receiving a higher quality material than many of the other fabrics on the market.  

This Pre-impregnated carbon fiber reinforcement makes part production efficient and allows for more complex parts to be produced vs standard infusion or vacuum bagging techniques as the epoxy is already in the fabric. The carbon material in the prepreg is our model F-374 11oz 6k 2x2 Twill weave that has been coated with epoxy. Prepreg is easier to use and allows you to piece sections together to create seams that look clean and professional. To use this material just cut to shape, pull off the plastic liner, place in mold, vacuum bag the material down and ramp up the heat to 250° F for one hour and your part is done. The material has a 42% resin/fiber ratio. This material is a double sided tack material meaning that there is resin on both sides of the material. This will allow for better adhesion between layers during the initial layup. The difference between single and double sided when laying up most parts is a personal preference on what is easier to use for that person. A single sided prepreg is typically used on the initial surface layer of the mold. To achieve a higher quality class A finish, we have surfacing films in clear for cosmetics and nylon reinforced for structural applications where parts will be painted.

This product is 50" wide and sold by the linear yard with a 5 yard minimum purchase required.

Shelf Life/Storage 

  • 0° F (standard freezer) - 1 Year
  • 40° F (standard fridge) - six months
  • 72° F (room temp) - 30 days.

It is suggested to store at 0° F or below to provide a longer shelf life. If you plan to use material faster, then you can store at a warmer temp to shorten the time it takes to get material to room temperature.

Cure time: Here is the cure schedule for a typical laminate (3-5 layers thick). On thicker laminates, you may want to slow the ramp time and hold the dwell time longer to ensure even heating throughout the part. Thermocouples on part will help you know actual part temperature and can speed up the curing process if needed.

  • Dwell at 100° F for 15min
  • Ramp Up to 150° F @ rate of 3° F/min
  • Dwell at 150° F for 30 min
  • Ramp Up to 200° F @ rate of 3° F/min
  • Dwell at 200° F for 30 min
  • Ramp Up to 250° F @ rate of 3° F/min
  • Dwell at 250° F for 1 Hour
  • Ramp Down to 200° F @ rate of 3° F/min
  • Dwell at 200° F for 30 min
  • Ramp Down to 150° F @ rate of 3° F/min
  • Dwell at 150° F for 30 min
  • Ramp Down to 100° F @ rate of 3° F/min
  • Finish

Application: Remove material from cold storage at least 20 hours prior to use so the material stabilizes at room temp. Keep the material wrapped to prevent moisture from condensing on the adhesive. Cut prepreg to the correct size, remove poly film from one side and apply to part or mold. Then remove the backing paper. Continue until the desired number of plies are obtained. When your lay-up is finished, you need to cure the material in a vacuum bag placed inside an oven or autoclave. Apply at least 10psi of pressure and 250° F for one hour.

Caution: This material contains epoxy resins and amines which may cause irritation to sensitive skin. Avoid contact with eyes or skin. If contact with skin occurs, wash as soon as possible with soap and water. If contact with eyes occurs, flush with water for 15 minutes. Do not handle or use this material until Material Safety Data Sheet has been read and understood. The user of this material is required to use the necessary protective equipment as directed by applicable state and federal laws when handling, curing, and grinding this material.

Shipping: This material should be shipped expedited airmail. Due to a short shelf life at room temp we suggest shipping this material via an expedited service such as UPS Overnight, 2-day or 3-day. These are guaranteed services. If these are chosen, we will ship the materials in the beginning of the week to ensure they do not sit in the shipping company warehouse over the weekend. We send the material with insulation and icepacks. It is suggested that you ship with 2-day airmail at a minimum. If you plan to use material within days of arrival or are OK with loosing days of shelf life, you can select any shipping method you would like, however if our minimum suggested shipping method is not chosen, we will not be held responsible for issues with material.

Custom Prepreg Options

We can have almost any of our fabrics pre-impregnated for you. Please email us for more details. We have systems that can cure at various temps from 200° F to 350° F. We can do a max width of 60". Lead times are usually 2-3 weeks for custom prepreg. We can do single side or double sided prepreg, vary the resin % in the cloth and vary the tack level of the material.

We take care in shipping our items and we will never fold the fabric. Our fabric is always rolled onto a tube to prevent distortion of the weave.

Resin Content Nominal 50% on 7781 glass, material can be supplied at other resin contents as required
Volatiles Less than 1%
Separator Release paper and poly film
Shelf Life One year at 0°F
Six months at 40°F
Thirty Days at 72°F
Material Warp Carbon Fiber
Material Weft Carbon Fiber
Weave 2x2 Twill
Ends Per Inch 11
Pics Per Inch 11
Yarn Size Warp 6k
Yarn Size Weft 6k
Tow Size 6k
Weight 11oz / 373gsm
Width 50" / 127cm
Thickness 0.017" / 0.43mm


Based upon 0.125 inch thick cured laminate consisting of PREG202S on 7781 glass cloth cured at 250°F (121°C) for one hour.
Mechanical Property Test Method Test Condition Test Values
Tensile Strength (ASTM D 638) @ 75°F dry 63,400 psi
Tensile Modulus (ASTM D 638) @ 75°F dry 3.5 X 106 psi
Compressive Strength (ASTM D 695) @ 75°F dry 48,600 psi
Flexural Strength (ASTM D 790) @ 75°F dry 80,100 psi
Flexural Modulus (ASTM D 790) @ 75°F dry 3.0 X 106 psi
Interlaminar Shear Strength (ASTM D 2344) @ 75°F dry 7,450 psi