Camouflage Carbon Fiber Black Aramid Hybrid 50" Width 6oz Remnant
NOTICE: The image may not represent the true color of this fabric. The Aramid material in this fabric is a Midnight Blue color not a true Black.
Camouflage Carbon Fiber/Black Aramid is a fabric that has been produced using beautiful Toray T-300 carbon fiber but has been woven in a special loom to create this amazing and unique pattern. These fabrics are still high strength materials but just have the added cosmetic appearance to make your parts stand out from the rest.
To harden the raw fabric into a usable form, you will need the appropriate resin or epoxy for your project.
Carbon Fiber / Aramid / Kevlar Hybrid fabrics.
This carbon fiber and aramid hybrid fabric combines the properties of both highly advanced fiber reinforcements. The carbon tow provides a very high level of strength and stiffness, while the aramid provides very good impact/abrasion/fracture resistance to the laminate layup. The aramid that is used in our cloth featuring colored aramid is DuPont Kevlar® while the natural or yellow aramid fabrics use either DuPont Kevlar or Lumat brand aramid. These fabrics are not just amazing looking cloths but combined with their unique weave patterns, they are ideal for usage in a wide variety of different applications. Many high-performance, high-impact applications can benefit from these materials such as boat building, automotive, military, racing, sporting goods and high strength paneling, just to name a few.
This material is suitable for just about any process that you would like to use. Like a simple wet-layup, or more advanced processes like vacuum infusion, vacuum bagging or RTM manufacturing processes. In addition to dry cloth, we are able to have this turned into prepreg for the advanced composite customer. This material is also highly sought after for parts that are being wrapped/skinned for just a single surface layer when trying to gain that cool composite look with an added reinforcement layer and not spending the time or money into creating tools for finished parts.
When using this material as a reinforcement in a part, you will want to use several layers of this fabric in each part. We also recommend rotating the composite layers to give the parts the same attributes in all directions. Non-structural components like body panels and covers will typically require only 1 or two layers of this cloth when combining this with other layers of reinforcement like standard carbon fiber or fiberglass fabrics.
First Quality Remnants:
First Quality Fabric Remnant Rolls are short rolls of fabric, which have no defects in them. These remnant rolls are either left over fabric from the end of a roll, or sections of fabric which were cut at the wrong length for a specific order. So instead of discarding the short roll, we package it up and sell it as a First Quality Remnant Roll. These First Quality Remnant Rolls are sold at 20% off of the retail price of that fabric.
Second Quality Remnants:
Second Quality Fabric Remnant Rolls are short rolls of fabric, which have a defect in the woven fabric in them. These remnant rolls are cut out of the standard fabrics we sell, but from sections of the rolls that have some defects in them. These defects make them not good to use if you want to make cosmetic parts, which have perfect woven fabric in them, but can be used as the inner layers of your parts, or if you are making small parts and can cut around the defects. These Second Quality Remnant Rolls are sold at 25% off of the retail price of that fabric.
All remnant rolls are rounded DOWN to the nearest ½ yard. So a remnant listed as 0.5 yards may actually be between 18” and 35” in length and a remnant listed at 2.0 yards may actually be between 72” and 89” in length.
|Unit of Measure||Piece|
|Material Warp||Carbon Fiber T-300/Black Aramid|
|Material Weft||Carbon Fiber T-300/Black Aramid|
|Ends Per Inch||13|
|Pics Per Inch||15|
|Yarn Size Warp||3k/1500d|
|Yarn Size Weft||3k/1500d|
|Weight||6oz / 203.43gsm|
|Width||50" / 127cm|
|Resin Consumption @ 45% Resin to Fabric by Weight||4.6opsy / 164.97gsm|
The resin consumption provided is for the approximate amount of resin by weight, contained in the final part after processing by vacuum infusion. This does not account for the resin used in the flow lines and consumables such as flow media or breather cloth. Wet-layup by hand will also have a higher resin consumption in the final part and is dependent upon users techniques. Vacuum bagging a wet layup will improve the resin content. Too much resin will cause a weaker part, NOT stronger. Average rule of thumb is around 45% (+/- a couple percent). To calculate actual resin % in your part a burn test is used. For example you have a part weighing 100 grams, you would burn off the resin which would leave the fiber behind. You should have 55 grams of fiber left when your process is working correctly. Due to the variables in processing it is hard to give an accurate amount of resin needed to purchase for making your part. However you will have waste no matter what method is used. A suggested ratio is about 1-1.5lbs of resin per lb of fabric purchased.