Camouflage Carbon Fiber 50" Width 6.5oz Toray T300
Camouflage carbon fiber is a fabric that has been produced using beautiful Toray T-300 carbon fiber but has been woven in a special loom to create this amazing and unique pattern. These fabrics are still high strength materials but just have the added cosmetic appearance to make your parts stand out from the rest.
To harden the raw fabric into a usable form, you will need the appropriate resin or epoxy for your project.
|Unit of Measure||Linear Yard|
|Material Warp||Carbon Fiber T300|
|Material Weft||Carbon Fiber T300|
|Ends Per Inch||13|
|Pics Per Inch||15|
|Yarn Size Warp||3k|
|Yarn Size Weft||3k|
|Weight||6.5oz / 220.39gsm|
|Width||50" / 127cm|
|Resin Consumption @ 45% Resin to Fabric by Weight||5.31opsy / 178.72gsm|
The resin consumption provided is for the approximate amount of resin by weight, contained in the final part after processing by vacuum infusion. This does not account for the resin used in the flow lines and consumables such as flow media or breather cloth. Wet-layup by hand will also have a higher resin consumption in the final part and is dependent upon users techniques. Vacuum bagging a wet layup will improve the resin content. Too much resin will cause a weaker part, NOT stronger. Average rule of thumb is around 45% (+/- a couple percent). To calculate actual resin % in your part a burn test is used. For example you have a part weighing 100 grams, you would burn off the resin which would leave the fiber behind. You should have 55 grams of fiber left when your process is working correctly. Due to the variables in processing it is hard to give an accurate amount of resin needed to purchase for making your part. However you will have waste no matter what method is used. A suggested ratio is about 1-1.5lbs of resin per lb of fabric purchased.