2nd Quality 2x2 Twill Carbon Fiber Fabric/Cloth 12k 19.7oz. This fabric is 50", tow size of 12k and is woven in a 2x2 twill weave. This is the most widely used pattern in the automotive industry. This material is woven tighter than most of our competitors' fabrics. This will help ensure a straight weave and a better looking final product.
NOTE: This is a 2nd Quality material.
Web-Lock is a fabric stabilization process that is achieved by applying high heat and pressure to lock every filament of fabric together, ensuring perfect cosmetic and structural symmetry. Currently, this process is ONLY offered by Composite Envisions. You may have seen or tried stabilized fabrics in the past, but we've found that these existing products can often be too stiff to work with, require large volume orders with high costs, or simply aren't available in the fabric or time frame needed. All these reasons lead us to one solution - Web-Lock. Web-Lock is the material that we believe solves all the current problems and exceeds the finished fabric performance on all levels. Web-Lock will help you improve your ease of manufacturing, saving you time and money.
The side that has the Web-Lock on it will not make a good finish for your parts as you will still be able to see the stabilizer in a finished part. When using make sure to have the stabilized side face the non cosmetic side of your part. If you have a part that requires to have a perfect finish on both side we would recommend using two layers of this material and face the stabilized sides together.
Advantages of Web-Lock
Web-Lock is applied at Composite Envisions, allowing flexibility of coating options. Currently, Web-Lock has been applied to Carbon Fiber, Kevlar, Fiberglass and will be available on other composite fibers.
Low MOQ's. Can be applied to smaller runs of fabric, up to full 100+ yd rolls.
Reduce employee training for the time it takes to make quality composites.
Reduce waste as a result of less damaged cloth.
Standard heat range is 225°F/107°C. Coatings can range from 194°F/90°C to 392°F/200°C (only capable now of doing up to 248°F/120°C material)
Current version only adds .175oz/6gsm of weight to the fabric for little interference. (weights available from 4-15gsm to change performance characteristics)
No release liner required between layers of material; reduces waste, lowers cost and makes material easier to use.
Compatible with most resin systems on the market, including polyester, vinylester and epoxy resin.
Can be applied to various widths ranging from narrow tapes to 50" wide.
Prevents fabric weave from shifting but stretches to allow the fabric to stay conformable.
Keeps fiber coverage even to avoid resin rich areas and failure points.
Produced in the USA. Our goal is to make Web-Lock the new standard for high-end composite fabrications meet your supply needs while exceeding your expectations.
To harden the raw fabric into a usable form, you will need the appropriate resin or epoxy for your project. For the colored materials, we suggest one of our resins which cure clear.
How we sell
This fabric is sold by the linear yard. The unit price displayed is for 1 linear yard, all volume discounts will be automatically applied when selecting larger quantities of fabric when added to your shopping cart, as indicated in the table above with quantity discount ranges for units purchased.
Please purchase the number of linear yards that you require. When purchasing multiple yards of the same fabric you will receive one continuous length of that material. We carefully take that material and roll it onto a cardboard core and wrap over with clear plastic or Kraft paper, making sure to keep the fabric in its first quality condition. We pride ourselves as having one of the best material handing crews possible. We have most of our material available for purchase in sample swatch books per fabric category. Samples of our fabrics can be purchased by Clicking this Link.
|Unit of Measure||Linear Yard|
|Material Warp||Carbon Fiber|
|Material Weft||Carbon Fiber|
|Ends Per Inch||11|
|Pics Per Inch||11|
|Yarn Size Warp||12k|
|Yarn Size Weft||12k|
|Weight||19.7oz / 667.95gsm|
|Thickness||0.03" / 0.76mm|
|Resin Consumption @ 45% Resin to Fabric by Weight||16.11opsy / 541.66gsm|
The resin consumption provided is for the approximate amount of resin by weight, contained in the final part after processing by vacuum infusion. This does not account for the resin used in the flow lines and consumables such as flow media or breather cloth. Wet-layup by hand will also have a higher resin consumption in the final part and is dependent upon users techniques. Vacuum bagging a wet layup will improve the resin content. Too much resin will cause a weaker part, NOT stronger. Average rule of thumb is around 45% (+/- a couple percent). To calculate actual resin % in your part a burn test is used. For example you have a part weighing 100 grams, you would burn off the resin which would leave the fiber behind. You should have 55 grams of fiber left when your process is working correctly. Due to the variables in processing it is hard to give an accurate amount of resin needed to purchase for making your part. However you will have waste no matter what method is used. A suggested ratio is about 1-1.5lbs of resin per lb of fabric purchased.