PRO-SET INF-114 Infusion Epoxy

Model: 1758

Starting at: $113.67

Please Choose:




  • Description
  • Details
  • Reviews

This listing is for PRO-SET INF-114 Infusion Resin only. You will need to select the appropriate PRO-SET Infusion Hardener from one of the suggested hardeners listed below.

PRO-SET INF-210 Fast Infusion Hardener - Pot Life: 27 min*

PRO-SET INF-211 Medium Infusion Hardener - Pot Life: 122 min*
PRO-SET INF-212 Slow Infusion Hardener - Pot Life: 185 min*
PRO-SET INF-213 Extra-Slow Infusion Hardener - Pot Life: 262 min*
PRO-SET INF-251-HT High-Temp Infusion Hardener - Pot Life: 380 min*

*Pot Life is calculated using 150g @ 77°F (25°C)

** If any of the above links do not take you to a product listing, it would indicate that product is not in stock.

infusion

PRO-SET Infusion Epoxies are super low viscosity systems with a range of hardeners to meet the demands of modern infusion processes.

proset

STANDARD INFUSION SYSTEMS

PRO-SET Infusion Epoxies accommodate a vast range of process needs with a single resin and four hardeners. PRO-SET Infusion hardeners range from fast to extra slow, and may be blended to provide even greater versatility with your custom processes.

Choose resin by viscosity and hardener by speed.

proset

Infusion Epoxies Hardeners may be blended for targeted cure time. Infusion process PRO-SET Infusion Epoxies result in lightweight, high performance composites that will withstand long term cyclic loading in the harshest environments. PRO-SET Infusion Epoxies develop excellent physical properties at room temperature and may be post-cured to further enhance performance.

proset

Infusion Epoxies can be dyed, upon request, to provide for visual quality control. A yellow dye in the resin and a blue dye in the hardener, when properly metered and thoroughly mixed, will result in a consistent shade of green.

INF Resin Selection

Property Standard Units INF-114 Resin1
Mix Ratio by Volume   R:H 3:1
Mix Ratio by Weight   R:H ~3.65:1
Mixed Viscosity @ 77°F (25°C) ASTM D2196 cP ~245
Mixed Density @ 72°F (22°C)   lb/gal (g/cc) ~9.52 (1.14)
Compression Yield ASTM D695 psi (MPa) ~14,100 (97.0)
Tensile Strength ASTM D638 psi (MPa) ~10,400 (71.7)
Tensile Modulus ASTM D638 psi (GPa) ~4.90E+05 (3.38)
Tensile Elongation ASTM D638 % ~4.95
Flexural Strength ASTM D790 psi (MPa) ~18,000 (124)
Flexural Modulus ASTM D790 psi (GPa) ~4.63E+05 (3.19)
Tg Ultimate via DMA2 ASTM E16403 °F (°C) >193 (85.2)
Tg Ultimate via DSC with INF-251-HT Hardener2 ASTM E16403 °F (°C) 264 (129)

1Average of properties for combinations with INF-210, INF-211, INF-212 and INF-213 Hardeners.
2 Additional post cure may be required; contact the Gougeon Technical Staff for details.
3 1 HZ, 3°C per minute

Typical Physical Properties Comparison Guide
Test specimens are cured at room temperature to gelation and 180°F (82°C) for eight hours, unless otherwise noted. Neat epoxy samples are used for testing. See Resin/Hardener Technical Data Sheet for exact values. Typical values, not to be construed as specifications.

MSDSPRO-SET INF-114 Epoxy MSDS

TDSPRO-SET INF-114 Epoxy with INF-210 Hardener TDS
TDSPRO-SET INF-114 Epoxy with INF-211 Hardener TDS
TDSPRO-SET INF-114 Epoxy with INF-212 Hardener TDS
TDSPRO-SET INF-114 Epoxy with INF-213 Hardener TDS
TDSPRO-SET INF-114 Epoxy with INF-251-HT Hardener TDS